The structures with BMIM guests (172 and 174) are generally blue-shifted by 15–20 nm than the structures with quaternary ammonium cations (171 and 175), and the corresponding lifetimes and quantum yields are significantly reduced.
The structures with BMIM guest (172 and 174) are generally 15-20 nm blueshifted than those with quaternary ammonium cation (171 and 175), and the corresponding lifetime and quantum yield are significantly reduced.
The structures (172 and 174) with BMIM guest are generally 15~20 nm bluer than the structures (171 and 175) with quaternary ammonium cations, and the corresponding lifetime and quantum yield are significantly reduced.